Waterproof And Anti-Seepage HDPE Smooth Geomembrane For Civil Engineering Projects
Product Introduction
Smooth geomembrane, also known as smooth geomembrane, is a widely used waterproof barrier geosynthetic material. The material is based on high molecular polymer, adding carbon black, antioxidant, anti-aging agent, ultraviolet absorber and color masterbatch and other auxiliary materials through special formula.
Product Properties
1. Low permeability: Smooth geomembrane has extremely low permeability, which can effectively prevent the passage of water and pollutants.
2. Chemical and ultraviolet resistance: Excellent chemical and ultraviolet resistance make the material resistant to various chemical substances and prolonged exposure to sunlight.
3. High cost performance: Compared with other similar products, smooth geomemofilm has a higher cost performance, is the first choice for civil engineering seepage prevention materials.
4. Strong adaptability: wide temperature adaptability, can be used in extreme weather conditions.
Product Application
1. Water conservancy and environmental protection: applied to the anti-seepage reinforcement of river dikes, lake DAMS, tailings DAMS, etc.
2. Municipal engineering: such as subway, building underground engineering, planting roof anti-seepage lining.
3. Aquaculture: Suitable for seawater, freshwater fish and shrimp farms.
4. Garden engineering: It can be used for waterproofing and moisture-proof of river, reservoir, artificial lake, etc.
5. Salt industry: salt field crystallization tank, halogen tank cover and other occasions.
6. Transportation infrastructure: waterproof layer of highway, railway foundation, etc.
7. Petrochemical industry: chemical plants, refineries, oil storage tank anti-seepage lining, etc.
8. Mining engineering: the bottom lining of washing pool, pile leaching pool, etc.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification |
0.75mm |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
Remark |
| Item |
| Thickness (mm) |
0.75mm |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
|
| Density (g/c㎡,≥) |
0.939 |
|
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) |
11 |
15 |
18 |
22 |
29 |
37 |
44 |
|
| Breaking Strength (N/mm,LD/TD) |
20 |
27 |
33 |
40 |
53 |
67 |
80 |
|
| Yeild Elongation Rate (%) |
12 |
|
| Breaking Elongation Rate (%) |
700 |
|
| Rectangular Tear Strength (N) |
93 |
125 |
156 |
187 |
249 |
311 |
374 |
|
| Puncture Strength (N) |
240 |
320 |
400 |
480 |
640 |
800 |
960 |
|
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) |
300 |
|
| Carbon Black |
| Carbon Black Content(Rang) (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 |
|
| Oxidative Induction Time (OIT) |
| Standard OIT (min) |
100 |
|
| High Pressure OIT (min) |
400 |
|
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) |
55 |
|
| 90 days after baking, the hight pressure OIT retention(%) |
80 |
|
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) |
50 |
|
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) |
50 |
|
| -70℃ The Low Temperature Embrittlement Performance mpact |
Pass |
|
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) |
≤1.0X10-13 |
|
| Dimensional Stability |
±2 |
|
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item |
0.30 |
0.50 |
0.75 |
1.00 |
1.25 |
1.50 |
2.00 |
2.50 |
3.00 |
Remark |
| Thickness (mm) |
0.30 |
0.50 |
0.75 |
1.00 |
1.25 |
1.50 |
2.00 |
2.50 |
3.00 |
|
| Density (g/c㎡,≥) |
0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) |
4 |
7 |
10 |
13 |
16 |
20 |
26 |
33 |
40 |
|
| Tensile Breaking Strength (N/mm, ≥,LD/TD) |
6 |
10 |
15 |
20 |
25 |
30 |
40 |
50 |
60 |
|
| Yield Elongation Rate (%,≥,LD/TD) |
- |
- |
- |
11 |
|
| Breaking Elongation Rate (%,≥,LD/TD) |
600 |
|
| Rectangular Tear Load (N,≥,LD/TD) |
34 |
56 |
84 |
115 |
140 |
170 |
225 |
280 |
340 |
|
| Puncture Strength (N,≥) |
72 |
120 |
180 |
240 |
300 |
360 |
480 |
600 |
720 |
|
| Carbon Black Content (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed |
|